SHOFU Beautifil II LS
Low-shrinkage paste composite for anterior and posterior restorations: beautifil II LS (Low Shrinkage), developed from the proven Beautifil II, guarantees dentists minimal shrinkage with maximum esthetics. The key feature of this universal paste composite is its exceptionally low polymerization shrinkage of only 0.85% by volume. It also features excellent polishability and natural shade adaptation to tooth structure. The material contains bioactive S-PRG fillers that act simultaneously as a source and reservoir of fluoride: depending on the fluoride concentration in the mouth, they release and replenish this trace element – for long-term, caries-protective restorative therapy.
When used in combination with BeautiBond, the perfectly matched all-in-one adhesive, the caries-protective effect of S-PRG filler technology is enhanced. Beautifil II LS achieves a well-balanced chameleon effect in both dentin and enamel thanks to its natural light reflection. This universal, light-cured composite polishes quickly and easily and has a long-lasting surface gloss.
Directions
- Direct restorations in the anterior and posterior sector
- Repairs of restorations and prosthetics
Advantages
- Low contraction (< 1%) and contraction tension
- Excellent polishability and long-lasting shine
- High abrasion resistance and surface hardness while respecting the antagonist
- Natural light transmission and diffusion
- Long-lasting fluoride release and recharge
- Color range identical to that of Beautifil II
Technical data
Polymerization shrinkage: 0.85% by volume according to ISO 17304:2013 (E)
Shrinkage stress: 10.9 MPa
Compressive strength: 364 MPa
Flexural strength: 117 MPa
Vickers hardness: 46 HV
Wear: 1.41% of weight
Filler concentration: 82.9% by weight
Curing depth: 2.4 mm
Radiopacity: 2.0 Al:mm