Katana ZR YML
THE ALL-IN-ONE SOLUTION. With KATANA™ Zirconia YML, you can cover the entire range of indications thanks to the combination of high translucency and high strength. SEAMLESS MULTILAYER STRUCTURE. KATANA™ Zirconia YML combines three different raw materials with different yttrium values for a balanced shade/translucency and flexural strength. ESTHETIC RESULTS WITH SIMPLICITY. The seamless multilayer technology eliminates visible transition lines, emphasizing natural color and translucency, with a simplified and fast procedure. ABSOLUTE STABILITY. The more precise fit of the restoration at the end of the final sintering process reduces the risk of having to perform rework. No wasted time and materials. FAST WORKING PROCESS. Rework or urgent cases? Rapid sintering (54 minutes) allows you to easily complete the job in one day.
Technical data
| Translucency: | ||
| Enamel: | Dentin 1: | Dentin 2, 3: |
| 49% | 47% | 45% |
| Bending strength: | ||
| Enamel: | Dentin 1: | Dentin 2, 3: |
| 750 MPa | 1,000 MPa | 1,100 MPa |
| Multilayer | ||
| Range of applications | Monolithic crowns | |
| Monolithic bridges | ||
| Cut-back structures | ||
| Directions | ||
| VENEER | 6/6 | |
| ONLAY / INLAY | 6/6 | |
| FRONT CROWN | 6/6 | |
| REAR CROWN | 6/6 | |
| 3-ELEMENT BRIDGE | 6/6 | |
| BRIDGE WITH MORE THAN 3 ELEMENTS | 6/6 | |
| Sintering programs: | 7 hours | |
| 90 minutes | ||
| 54 minutes | ||
| Layering with: | CZR™ FC Paste Stain | |
| CZR™ Internal Stain | ||
| CZR™ Ceramic | ||
| Micro-stratification with: | Technique 4.4.1 |