Katana ZR YML
THE ALL-IN-ONE SOLUTION. With KATANA™ Zirconia YML it is possible to cover the entire range of indications thanks to the combination of high translucency and high resistance. MULTI-LAYER STRUCTURE WITHOUT CONTINUITY. KATANA™ Zirconia YML combines three different raw materials with different yttrium values for a balanced gradation of color/translucency and flexural strength. AESTHETIC RESULTS WITH SIMPLICITY. Seamless multi-layer technology eliminates visible transition lines, emphasizing natural color and translucency, with a simplified and fast procedure. ABSOLUTE STABILITY. The more precise fit of the restoration at the end of the final sintering process reduces the risk of having to carry out rework. No waste of time and materials. QUICK MACHINING PROCESS. Rework or urgent cases? Fast sintering (54 minutes) allows you to easily get the job done in one day.
Technical data
| Translucency: | ||
| Enamel: | Dentin 1: | Dentin 2, 3: |
| 49% | 47% | 45% |
| Flexural strength: | ||
| Enamel: | Dentin 1: | Dentin 2, 3: |
| 750 MPa | 1,000 MPa | 1,100 MPa |
| Multilayer | ||
| Range of applications | Monolithic crowns | |
| Monolithic bridges | ||
| Cut-back structures | ||
| Directions | ||
| VENEER | 6/6 | |
| ONLAY / INLAY | 6/6 | |
| FRONT CROWN | 6/6 | |
| REAR CROWN | 6/6 | |
| 3-ELEMENT BRIDGE | 6/6 | |
| BRIDGE WITH MORE THAN 3 ELEMENTS | 6/6 | |
| Sintering programs: | 7 hours | |
| 90 minutes | ||
| 54 minutes | ||
| Layering with: | CZR™ FC Paste Stain | |
| CZR™ Internal Stain | ||
| CZR™ ceramic | ||
| Micro-layering with: | Technique 4.4.1 |